Metal‑Ceramic Composites Rod

Ultra-High Wear Resistance

Surface hardness HRA 90–95; wear resistance 3–5 times higher than conventional steel, greatly extending service life.

High Temperature & Corrosion Resistance

Withstands temperatures up to 1200°C (in inert atmosphere) and resists strong acids, alkalis, and salt spray.

Lightweight & High Stiffness

Density: 60%–70% of traditional alloys; compressive strength >1500 MPa, ideal for precision instruments.

Wide Application Coverage

Machinery: bearings, guide rails, cutting tools, wear parts

Electronics: semiconductor packaging supports, high-frequency circuit substrates

Energy & Chemical: pump/seal parts, reactor liners

Aerospace: high-temp engine components, lightweight structures

vacuum hot‑press sintering, plasma spraying

Customizable size, material ratio and surface finishing

Standard 2 weeks; military custom 4–8 weeks.

One-stop guidance from selection to installation

Parameter	Specification
Material Composition	Metal matrix (titanium alloy / stainless steel) + Al₂O₃/ZrO₂ ceramic particles
Density	4.5–6.2 g/cm³
Hardness	HRA 90–95
Compressive Strength	≥1500 MPa
Max Working Temp	≤1200°C (inert atmosphere)
CTE (20–800°C)	8.5–11.5×10⁻⁶/°C
Corrosion Resistance	ISO 9227 salt spray test ≥500 hours